The low-temperature sinterability of TiO₂-CuO systems was investigated using a solid solution of SnO₂. Sample powders were prepared through conventional ball milling of mixed raw powders. With the SnO₂ content, the compositions of the samples were Ti_1-xSn_xO₂-CuO(2 wt.%) in the range of x ≤ 0.08. Compared with the samples without SnO₂ addition, the densification was enhanced when the samples were sintered at 900°C. The dominant mass transport mechanism seemed to be grain-boundary diffusion during heat treatment at 900°C, where active grain-boundary diffusion was responsible for the improved densification. The rapid grain growth featured by activated sintering was also obstructed with the addition of SnO₂. This suggested that both CuO as an activator and SnO₂ dopant synergistically reduced the sintering temperature of TiO₂.

The green body of WC-Co cemented carbides containing polymeric binders such as paraffin, polyethylene glycol (PEG), and polyvinyl acetate (PVA) are prepared. The green density of the WC-Co cemented carbides increases with the addition of binders, with the exception of PVA, which is known to be a polar polymeric substance. The green strength of the WC-Co cemented carbides improves with the addition of paraffin and a mixture of PEG400 and PEG4000. In contrast, the green strength of the WC-Co does not increase when PEG400 and PEG4000 is added individually. The compressive strength of the green body increases to 14 MPa, and the machinability of the green body improves when more than 4–6 wt% paraffin and a mixture of PEG400 and PEG4000 is used. Simultaneously, the sintered density of WC-Co is as high as 99% relative density, similar to a low binder addition of 1–2 wt%.